Effect of different ceramic systems on antagonist dental structure by microtomographic analysis.

OBJECTIVES: This study aims to identify the two-dimensional and three-dimensional analyses and evaluate the loss of tooth structure in the tooth's different constituent elements and the ceramic antagonist's surface. METHODS: In this study, three groups (n = 10) represented by different ceramic systems (lithium disilicate [GDis], lithium silicate reinforced with zirconia [GSil], and monolithic zirconia [GZir]) were evaluated. Each group obtained ten ceramic blocks and submitted them to the sintering/crystallization process. To carry out the wear test, healthy mandibular premolars were used as the specimens and the ceramic blocks as antagonists. The premolars were submitted to two-dimensional and three-dimensional analyses using a computerized microtomography (µTC) before and after the wear test. The wear test was performed with 30 N and 300,000 cycles load, with occlusion, laterality, and disocclusion movements. RESULTS: The statistical analysis comparing the loss of two-dimensional tooth structure showed a statistically significant difference among all groups (p < 0.05). Statistical analysis comparing the percentage of loss of three-dimensional tooth structure showed a statistically significant difference between groups GDis and GSil and between groups GDis and GZir. However, when comparing GSil with GZir, no statistically significant difference was found. The qualitative analysis of the teeth showed that GDis showed considerable enamel loss and dentin exposure, GSil showed enamel wear with flattening the cusp without dentin exposure, and GZir showed minimal enamel wear without dentin exposure. In the qualitative analysis of ceramic antagonists, more significant wear of the ceramic material for GDis was observed, followed by the GSil and GZir groups, respectively. SIGNIFICANCE: The use of the lithium disilicate should be cautious, restricting it to areas with lower masticatory forces. Areas of higher masticatory forces showed a large amount of antagonist wear, with dentin involvement. This can lead to dentinal hypersensitivity, risk of compromising patients' occlusion, by harming group disocclusion guides, causing pain and temporomandibular disorders.

Is the Er:YAG laser affect the surface characteristics and bond strength of Y-TZP?

Abstract This study evaluated the surface characteristics and bond strength of Y-TZP treated with Er:YAG laser at different focal distances. 120 Y-TZP blocks were divided into five groups (n=24), according to the surface treatment: no treatment (C-); sandblasting with silica-coated aluminum oxide particles (C+); and Er:YAG laser application at focal distances of 1mm (Er:YAG-1), 4mm (Er:YAG-4), and 7mm (Er:YAG-7). Surface characteristics were analyzed using Vickers microhardness, confocal laser microscope, scanning electron microscopy (SEM), and X-ray diffractometer (XRD). For the bond strength test, 100 Y-TZP blocks were subdivided into two subgroups (n=10), according to the resin cement used: with (MDP+) or without 10-methacryloyloxydecyl dihydrogen phosphate (MDP-). The Vickers microhardness and surface roughness were analyzed by one-way ANOVA and bond strength by two-way ANOVA and Tukey's test for both (α=0.05). Vickers microhardness differences were not observed between the groups (p>0.05); C+ showed higher surface roughness values. SEM images showed micromorphological differences between the groups. The XRD data detected tetragonal crystals for C- and, for the other groups, tetragonal and monoclinic peaks. For bond strength, no statistically difference significance were observed among the cements with or without MDP (p>0.05) but showed significant difference between the surface treatments (C+ > C- = Er:YAG1 > Er:YAG4 = Er:YAG7) (p<0.05). Suggested that the Er:YAG laser cannot replace conventional treatment with aluminum oxide particles and the presence of MDP in the resin cement had no influence on the bond strength.

Resumo Este estudo avaliou as características de superfície e resistência de união de Y-TZP tratado com laser de Er: YAG em diferentes distâncias focais. Cento e vinte blocos de Y-TZP foram divididos em cinco grupos (n=24), de acordo com a superfície de tratamento: sem tratamento (C-); asperização com partículas de óxido de alumínio revestidas por sílica (C +); e aplicação de laser Er: YAG a distâncias focais de 1 mm (Er: YAG-1), 4 mm (Er: YAG-4) e 7 mm (Er: YAG-7). As características de superfície foram analisadas por meio de microdureza Vickers, microscópio confocal a laser, microscopia eletrônica de varredura (MEV) e difratômetro de raios-X (DRX). Para o ensaio de resistência de união, cem blocos de Y-TZP foram subdivididos em 2 subgrupos (n=10) de acordo com o cimento resinoso utilizado (n=12): com 10-metacriloiloxidecil dihidrogenofosfato (MDP+) ou sem (MDP-). Microdureza Vickers e rugosidade de superfície foram analisadas por ANOVA a 1 fator e a resistência de união por ANOVA a 2 fatores e ambos seguidos de teste complementar de Tukey (α=0,05). Não foram observadas diferenças de microdureza Vickers entre os grupos; C+ apresentou maiores valores de rugosidade superficial. Imagens de MEV mostraram diferenças micromorfológicas entre os grupos. Os dados de DRX detectaram apenas cristais tetragonais para C- e, para os outros grupos, picos de zircônia nas fases tetragonal e monoclínica. Para a resistência de união, não foram observadas diferenças estatisticamente significante entre os cimentos com e sem MDP (p>0.05), mas foram observadas diferenças significativas entre os tratamentos de superfície (C+ > C- = Er:YAG1 > Er:YAG4 = Er:YAG7) (p<0.05). Sugere-se que o laser de Er: YAG não pode substituir o tratamento convencional com partículas de óxido de alumínio e a presença de MDP no cimento resinoso não influenciou na resistência de união.

Is the Er:YAG laser affect the surface characteristics and bond strength of Y-TZP?

This study evaluated the surface characteristics and bond strength of Y-TZP treated with Er:YAG laser at different focal distances. 120 Y-TZP blocks were divided into five groups (n=24), according to the surface treatment: no treatment (C-); sandblasting with silica-coated aluminum oxide particles (C+); and Er:YAG laser application at focal distances of 1mm (Er:YAG-1), 4mm (Er:YAG-4), and 7mm (Er:YAG-7). Surface characteristics were analyzed using Vickers microhardness, confocal laser microscope, scanning electron microscopy (SEM), and X-ray diffractometer (XRD). For the bond strength test, 100 Y-TZP blocks were subdivided into two subgroups (n=10), according to the resin cement used: with (MDP+) or without 10-methacryloyloxydecyl dihydrogen phosphate (MDP-). The Vickers microhardness and surface roughness were analyzed by one-way ANOVA and bond strength by two-way ANOVA and Tukey's test for both (α=0.05). Vickers microhardness differences were not observed between the groups (p>0.05); C+ showed higher surface roughness values. SEM images showed micromorphological differences between the groups. The XRD data detected tetragonal crystals for C- and, for the other groups, tetragonal and monoclinic peaks. For bond strength, no statistically difference significance were observed among the cements with or without MDP (p>0.05) but showed significant difference between the surface treatments (C+ > C- = Er:YAG1 > Er:YAG4 = Er:YAG7) (p<0.05). Suggested that the Er:YAG laser cannot replace conventional treatment with aluminum oxide particles and the presence of MDP in the resin cement had no influence on the bond strength.

Influence of different ceramic materials and surface treatments on the adhesion of Prevotella intermedia.

Ceramics are used in oral rehabilitation; however, these materials are prone to formation of biofilms that may cause periodontal diseases. This study aimed to evaluate the influence of distinct surface treatments on ceramic surface roughness and biofilm formation of oral bacteria (Prevotella intermedia). Eighty-four specimens of the following four ceramic systems were produced: LC - leucite-based glass ceramic, LD - lithium disilicate-based glass ceramic, LSZ - glass ceramic based on zirconia-reinforced lithium silicate, and ZR - monolithic zirconia. These were submitted to three different surface treatment protocols: C - control, G - glazing, and GDB - grinding with diamond bur (n = 7). The surface characteristics were assessed using a confocal laser microscope (Ra) and a scanning electron microscope (SEM). Thereafter, the groups were contaminated with a bacterial strain of P. intermedia ATCC 25611. The biofilms formed were quantified by counting the colony forming units (CFUs) and analyzed with scanning electron microscope (SEM) and confocal laser scanning microscope (CLSM). Data were analyzed by using a 2-way ANOVA and the Tukey test (ɑ = 0.05). Results showed that greater roughness was associated with GDB (p < 0.05). The same was also true for the ceramic material ZR (p < 0.05). There was a statistical significant difference in the CFU counts between the materials (p < 0.05) that revealed a greater amount of bacterial adhesion in the LC and ZR groups (p > 0.05). Thus, it was suggested that the surface roughness of the ceramic materials favored bacterial adhesion; and thus, finishing of ceramic surfaces with GDB should be avoided.

Effect of restorative treatment with endocrown and ferrule on the mechanical behavior of anterior endodontically treated teeth: An in vitro analysis.

This study evaluated the effect of endocrown and ferrule restorative treatment on the mechanical behavior of anterior endodontically treated teeth. Human canines were treated endodontically and distributed in five groups (n = 10): sound teeth (S), crown associated with glass fiber post (GFP) and ferrule (GFPf+) and that without ferrule (GFPf-), and endocrown with ferrule (Ef+) and that without ferrule (Ef-). The crowns were obtained in lithium disilicate-based glass ceramic and cemented with resin. Thermomechanical loading (TL) was performed with progressive load of 80, 120, 160, 200, 240, 280, and 320 N with 20,000 cycles each, 140,000 cycles in total, frequency of 5 Hz, and temperature variation of 5°C-55 °C, followed by fracture resistance testing with load cell of 1000 Kgf and crosshead speed of 0.5 mm/min in a universal testing machine. Failure mode has been evaluated. Data were compared by Kaplan-Meier survival analysis (p < 0.05) for TL and one-way ANOVA and Tukey's test (p < 0.05) for fracture resistance. TL showed higher number of fractures for groups without ferrule (GFPf- = 7, GFPf+ = 3, Ef- = 10, and Ef+ = 2) and lower mean fracture load probability (GFPf+ = 300 N, GFPf- = 280 N, Ef+ = 320 N, Ef- = 188 N) than those with ferrule. Regarding fracture, teeth rehabilitated with GFP were more resistant to endocrowns with ferrule (p < 0.05). A higher percentage of type III failures after fatigue and type II failures after fracture were found. In conclusion, rehabilitation using GFP with ferrule is more favorable for anterior teeth, but the use of endocrown with ferrule proved feasible.

Effect of different grinding protocols on surface characteristics and fatigue behavior of yttria-stabilized zirconia polycrystalline: An in vitro study.

STATEMENT OF PROBLEM: Zirconia frameworks milled by computer-aided design and computer-aided manufacturing (CAD-CAM) often require clinical adjustments. In addition, zirconia prefabricated abutments can also require customization to achieve an adequate emergence profile. However, the influence of grinding adjustment on the surface characteristics and mechanical behavior of yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) and the best grinding protocol is unclear. PURPOSE: The purpose of this in vitro study was to evaluate the effect of different grinding protocols on the surface characteristics, phase transformation, and mechanical behavior of Y-TZP for frameworks and implant abutments. MATERIAL AND METHODS: Bar-shaped specimens were fabricated according to ISO 6872-2016 and divided into 3 groups: GC (control, untreated), GA (grinding and finishing with medium and fine diamond rotary instruments using high-speed handpiece under constant water cooling), and GB (grinding and finishing with coarse and medium diamond rotary instruments, respectively, using slow-speed handpiece without water cooling). After specimen grinding, the topography and surface roughness were evaluated by using a laser confocal microscope, the Young modulus was measured by the impulse excitation technique, and crystallographic phase transformation was analyzed by X-ray diffraction. Specimens were then submitted to step-stress accelerated life testing (n=18). The surface roughness and Young modulus results were analyzed by 1-way ANOVA and the Tukey honestly significant difference test (α=.05). The data of step-stress accelerated life testing were analyzed by the survival probability considering the number of cycles and force until fracture. RESULTS: Statistically significant differences were found among groups considering surface roughness (GA>GB>GC) (P<.05) and Young modulus (GB>GA=GC) (P=.003). X-ray diffraction showed that grinding leads to phase transformation, GC showed only tetragonal phase, while GA and GB showed tetragonal and monoclinic phases. No statistically significant difference (P<.05) was found among groups submitted to the same loading profile when the survival probability was compared, but significant difference was found between the light and moderate loading (P=.002) and light and severe loading (P=.014) of GB when different loading profiles in each group were compared. CONCLUSIONS: Although grinding protocols affected surface characteristics and promoted phase transformation, the mechanical behavior of Y-TZP was not impaired. Therefore, both the grinding protocols tested can be safely used based on the evaluated properties.

Influence of Manufacturing Methods of Implant-Supported Crowns on External and Internal Marginal Fit: A Micro-CT Analysis.

AIM: To evaluate the influence of different manufacturing methods of single implant-supported metallic crowns on the internal and external marginal fit through computed microtomography. METHODS: Forty external hexagon implants were divided into 4 groups (n = 8), according to the manufacturing method: GC, conventional casting; GI, induction casting; GP, plasma casting; and GCAD, CAD/CAM machining. The crowns were attached to the implants with insertion torque of 30 N·cm. The external (vertical and horizontal) marginal fit and internal fit were assessed through computed microtomography. Internal and external marginal fit data (µm) were submitted to a one-way ANOVA and Tukey's test (α = .05). Qualitative evaluation of the images was conducted by using micro-CT. RESULTS: The statistical analysis revealed no significant difference between the groups for vertical misfit (P = 0.721). There was no significant difference (P > 0.05) for the internal and horizontal marginal misfit in the groups GC, GI, and GP, but it was found for the group GCAD (P ≤ 0.05). Qualitative analysis revealed that most of the samples of cast groups exhibited crowns underextension while the group GCAD showed overextension. CONCLUSIONS: The manufacturing method of the crowns influenced the accuracy of marginal fit between the prosthesis and implant. The best results were found for the crowns fabricated through CAD/CAM machining.

Evaluation of Stress Distribution in Endodontically Weakened Teeth Restored with Different Crown Materials: 3D-FEA Analysis.

This study evaluated the stress distribution in endodontically treated teeth, weakened (W) or not weakened (NW), restored with different materials of prosthetic crown using 3D-FEA. Models of a maxillary canine were constructed based on micro-CT images and divided into the groups: G1 (control) - sound tooth; G2 to G7 - endodontically treated teeth restored with glass fiber post (GFP); which G2 to G4 simulated NW root and G5 to G7 simulated W root. For crown material the teeth were restored with: G2 and G5: metallic coping and ceramic veneering, G3 and G6: zirconia coping and ceramic veneering, G4 and G7: alumina coping and ceramic veneering. Load of 180 N was applied at the incisal third of lingual surface at 45º. Models were supported by the periodontal ligament (x=y=z=0). The von Mises stress (VMS) values were calculated. The W teeth presented higher VMS at coping when compared to NW teeth and group G1 showed lower VMS value. For crown material, for both W or NW teeth, increasing VMS was found at metallic, zirconia and alumina coping, respectively. Metallic coping showed a better performance despite its unfavorable esthetics, suggesting as an appropriate material for prosthetic restoration of endodontically treated teeth.